Dry photochemical selective etching of InGaAs/InAlAs in HBr gas using a 172 nm excimer lamp

Soheil Habibi, Masahiro Totsuka, Jun Tanaka, Takeshi Kinoshita, Satoru Matsumoto, S. Iida

Research output: Contribution to journalArticlepeer-review

6 Citations (Scopus)


A new dry photochemical etching process using HBr gas to selectively remove InGaAs layer over an InAlAs layer has been developed. A 172 nm Excimer lamp was used as the photon source for this experiment. The intensity of the 172 nm light on the surface of the samples was 3 mW/cm2. Etch rates of 62 angstrom/min and 0.61 angstrom/min are obtained for InGaAs and InAlAs, respectively, at a chamber pressure of 120 mTorr, sample temperature of 80 °C and HBr flow rate of 10 sccm. These rates translate into a selectivity of over 100 for this material system. Scanning electron microscopy pictures and visual inspection reveal that this process is almost damage free, compared to reactive ion etching. This is due to lack of ion bombardment in the photochemical process. X-ray photoelectron spectroscopy analysis suggests that the etch selectivity mechanism is due to the formation of nonvolatile Al2O3 on the surface of the InAlAs layer. This etching system should be very useful for fabrication of electrical as well as optical devices based on InGaAs/InAlAs heterojunction.

Original languageEnglish
Pages (from-to)247-252
Number of pages6
JournalJournal of Vacuum Science and Technology B: Microelectronics and Nanometer Structures
Issue number2
Publication statusPublished - 1995 Mar

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Electrical and Electronic Engineering


Dive into the research topics of 'Dry photochemical selective etching of InGaAs/InAlAs in HBr gas using a 172 nm excimer lamp'. Together they form a unique fingerprint.

Cite this