Enhanced photoelectrochemical performance of ZnO electrodes sensitized with N-719

Keita Kakiuchi; Eiji Hosono; Shinobu Fujihara

doi:10.1016/j.jphotochem.2005.07.018

Enhanced photoelectrochemical performance of ZnO electrodes sensitized with N-719

Keita Kakiuchi
, Eiji Hosono
, Shinobu Fujihara

Department of Applied Chemistry

Research output: Contribution to journal › Article › peer-review

224 Citations (Scopus)

Abstract

To improve dye-loading in photoanodes, microstructure of ZnO films was modified through the formation and pyrolysis of layered hydroxide zinc acetate (LHZA) grown in a methanolic solution of zinc acetate dihydrate. Appropriate annealing treatments for the films led to the formation of mesoporous microstructure with an average pore diameter of 12 nm. It was demonstrated that loading of N-719 in the ZnO films was successful without influence of protons in solutions, as evidenced by a large dye amount of 1.4 × 10^-7 mol/cm², and hence a high short-circuit photocurrent density of 12.6 mA/cm². Sandwich-type dye-sensitized solar cells using the present ZnO/N-719 photoanode exhibited a conversion efficiency as high as 4.1% (AM-1.5, 100 mW/cm²).

Original language	English
Pages (from-to)	81-86
Number of pages	6
Journal	Journal of Photochemistry and Photobiology A: Chemistry
Volume	179
Issue number	1-2
DOIs	https://doi.org/10.1016/j.jphotochem.2005.07.018
Publication status	Published - 2006 Apr 1

Keywords

Conversion efficiency
Dye-sensitized solar cells
Microstructure
N-719
Zinc oxide

ASJC Scopus subject areas

General Chemistry
General Chemical Engineering
General Physics and Astronomy

Access to Document

10.1016/j.jphotochem.2005.07.018

Cite this

@article{94ca60d921014e1d98da4035006b0a78,

title = "Enhanced photoelectrochemical performance of ZnO electrodes sensitized with N-719",

abstract = "To improve dye-loading in photoanodes, microstructure of ZnO films was modified through the formation and pyrolysis of layered hydroxide zinc acetate (LHZA) grown in a methanolic solution of zinc acetate dihydrate. Appropriate annealing treatments for the films led to the formation of mesoporous microstructure with an average pore diameter of 12 nm. It was demonstrated that loading of N-719 in the ZnO films was successful without influence of protons in solutions, as evidenced by a large dye amount of 1.4 {\texttimes} 10-7 mol/cm2, and hence a high short-circuit photocurrent density of 12.6 mA/cm2. Sandwich-type dye-sensitized solar cells using the present ZnO/N-719 photoanode exhibited a conversion efficiency as high as 4.1\% (AM-1.5, 100 mW/cm2).",

keywords = "Conversion efficiency, Dye-sensitized solar cells, Microstructure, N-719, Zinc oxide",

author = "Keita Kakiuchi and Eiji Hosono and Shinobu Fujihara",

note = "Funding Information: This work was financially supported by Amano Foundation, Shizuoka, Japan.",

year = "2006",

month = apr,

day = "1",

doi = "10.1016/j.jphotochem.2005.07.018",

language = "English",

volume = "179",

pages = "81--86",

journal = "Journal of Photochemistry and Photobiology A: Chemistry",

issn = "1010-6030",

publisher = "Elsevier B.V.",

number = "1-2",

}

TY - JOUR

T1 - Enhanced photoelectrochemical performance of ZnO electrodes sensitized with N-719

AU - Kakiuchi, Keita

AU - Hosono, Eiji

AU - Fujihara, Shinobu

N1 - Funding Information: This work was financially supported by Amano Foundation, Shizuoka, Japan.

PY - 2006/4/1

Y1 - 2006/4/1

N2 - To improve dye-loading in photoanodes, microstructure of ZnO films was modified through the formation and pyrolysis of layered hydroxide zinc acetate (LHZA) grown in a methanolic solution of zinc acetate dihydrate. Appropriate annealing treatments for the films led to the formation of mesoporous microstructure with an average pore diameter of 12 nm. It was demonstrated that loading of N-719 in the ZnO films was successful without influence of protons in solutions, as evidenced by a large dye amount of 1.4 × 10-7 mol/cm2, and hence a high short-circuit photocurrent density of 12.6 mA/cm2. Sandwich-type dye-sensitized solar cells using the present ZnO/N-719 photoanode exhibited a conversion efficiency as high as 4.1% (AM-1.5, 100 mW/cm2).

AB - To improve dye-loading in photoanodes, microstructure of ZnO films was modified through the formation and pyrolysis of layered hydroxide zinc acetate (LHZA) grown in a methanolic solution of zinc acetate dihydrate. Appropriate annealing treatments for the films led to the formation of mesoporous microstructure with an average pore diameter of 12 nm. It was demonstrated that loading of N-719 in the ZnO films was successful without influence of protons in solutions, as evidenced by a large dye amount of 1.4 × 10-7 mol/cm2, and hence a high short-circuit photocurrent density of 12.6 mA/cm2. Sandwich-type dye-sensitized solar cells using the present ZnO/N-719 photoanode exhibited a conversion efficiency as high as 4.1% (AM-1.5, 100 mW/cm2).

KW - Conversion efficiency

KW - Dye-sensitized solar cells

KW - Microstructure

KW - N-719

KW - Zinc oxide

UR - https://www.scopus.com/pages/publications/33644785028

UR - https://www.scopus.com/pages/publications/33644785028#tab=citedBy

U2 - 10.1016/j.jphotochem.2005.07.018

DO - 10.1016/j.jphotochem.2005.07.018

M3 - Article

AN - SCOPUS:33644785028

SN - 1010-6030

VL - 179

SP - 81

EP - 86

JO - Journal of Photochemistry and Photobiology A: Chemistry

JF - Journal of Photochemistry and Photobiology A: Chemistry

IS - 1-2

ER -

Enhanced photoelectrochemical performance of ZnO electrodes sensitized with N-719

Abstract

Keywords

ASJC Scopus subject areas

Access to Document

Other files and links

Fingerprint

Cite this