Luminescence of Cr³⁺ ions associated with surpassing the green-emissive defect centers in β-Ga₂O₃

Photoluminescence of undoped and Cr³⁺-doped β-Ga₂O₃ was investigated. The transparent, undoped β-Ga₂O₃ film was successfully prepared by thermal conversion from GaOOH. The film exhibited predominant green luminescence in response to ultraviolet light excitation at 250 nm. This luminescence behavior, which was proposed to result from the oxygen defect centers, was used in examining excitation and emission mechanisms for Cr³⁺ ions doped in β-Ga₂O₃. It was found that red luminescence of Cr³⁺ surpasses green luminescence of the host lattice, as evidenced by the dependence of the spectral structure on the Cr³⁺ concentration. The excitation of Cr³⁺ was then suggested to be caused by the energy transfer from Ga³⁺O₆ octahedra present in the monoclinic β-Ga₂O₃ lattice.