Sol-gel processing of BaMgF4-Eu2+ thin films and their violet luminescence

S. Fujihara, Y. Kishiki, T. Kimura

Research output: Contribution to journalArticlepeer-review

27 Citations (Scopus)


BaMgF4-Eu2+ thin films were prepared from trifluoroacetate precursor solutions by a sol-gel method and their violet luminescence was investigated. A (Ba,Eu)MgF4 phase was obtained by heating the spin-coated precursor films at temperatures of 550-650°C. The reduction of Eu3+, which originated from Eu(CH3COO)3·4H2O in the precursor, to Eu2+ in the heat-treated films was evidenced by the strong, broadband 4f-5d excitation at 290 nm and emission at 420 nm in photoluminescence measurements. The intensity of violet luminescence of Eu2+ depended on the heating temperature, heating time and the Eu concentration. The strongest violet emission was observed with the BaMgF4-Eu (15 mol%) film that was heated at 650°C for 10 min under the present experimental conditions.

Original languageEnglish
Pages (from-to)76-80
Number of pages5
JournalJournal of Alloys and Compounds
Issue number1-2
Publication statusPublished - 2002 Feb 14


  • Chemical synthesis
  • Luminescence
  • Phosphors
  • Thin films

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry


Dive into the research topics of 'Sol-gel processing of BaMgF4-Eu2+ thin films and their violet luminescence'. Together they form a unique fingerprint.

Cite this