Change Behavior of Retained Austenite and Residual Stress on Carburized SCM420H Steel during Fatigue Process

Motoaki Hayama, Yusuke Maki, Shoichi Kikuchi, Jun Komotori

研究成果: Article査読

2 被引用数 (Scopus)

抄録

The transformation behavior of retained austenite in carburized SCM420H steel and its effect on the change in residual stress on a surface are investigated. The retained austenite on the carburized steel is transformed significantly in the first cycle of fatigue loading with a stress ratio of −1, and the transformation is less significant thereafter. Tensile loading significantly affects the transformation of retained austenite as compared with compressive loading. This is because the mechanical driving force that contributes to the martensitic transformation of retained austenite differs under tensile and compressive stresses. To investigate the transformation behavior of retained austenite and residual stress more comprehensively, an in situ X-ray measurement of retained austenite and residual stress is conducted. In the measurement, retained austenite or residual stress on a specimen surface is measured under loading conditions. Results show that the transformation of retained austenite under tensile loading involves a threshold stress value at which the transformation begins. The transformation of retained austenite proceeds when the applied stress exceeds the threshold value; however, no transformation occurs regardless of the number of loading cycles when the applied stress does not exceed the threshold. The compressive residual stress on the specimen surface increases as retained austenite transforms to martensite due to stress loading.

本文言語English
ページ(範囲)597-604
ページ数8
ジャーナルISIJ International
64
3
DOI
出版ステータスPublished - 2024

ASJC Scopus subject areas

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Change Behavior of Retained Austenite and Residual Stress on Carburized SCM420H Steel during Fatigue Process」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル