Effects of annealing on CuInSe2 films grown by molecular beam epitaxy

S. Niki, I. Kim, P. J. Fons, H. Shibata, A. Yamada, H. Oyanagi, T. Kurafuji, S. Chichibu, H. Nakanishi

研究成果: Article査読

12 被引用数 (Scopus)


CuInSe2 (CIS) thin films with a range of Cu/In ratios were grown by molecular beam epitaxy on GaAs (0 0 1) at substrate temperatures of Ts = 450-500°C and the effects of annealing under various atmospheres have been investigated. Photoluminescence spectra obtained from an ex-situ vacuum annealed CIS film at a temperature of TA = 350°C showed a red-shift and a broadening of an emission peak (peak c) which originally appeared at 0.970 eV before annealing and the red-shifted peak c was found to consist of two overlapping peaks. The excitation power dependence of these overlapping peaks indicated the radiative recombination processes associated with the emissions to be a conduction band to acceptor transition (peak at 0.970 eV) and a transition due to donor-acceptor pairs (peak at 0.959 eV), indicating the formation of a shallow donor-type defect during the vacuum annealing process. The origin of this defect has tentatively been attributed to Se vacancies. On the other hand, the molar fraction of oxygen increased with increasing annealing temperature in dry-air. An epitaxially grown In2O3 phase was found both in Cu-rich and In-rich films annealed at TA ≥ 350°C, which was not observed in the films annealed in Ar atmosphere. Thermodynamic calculations based on the Cu-In-Se-O-N system showed In2O3 to be the most stable phase in good agreement with the experimental results.

ジャーナルSolar Energy Materials and Solar Cells
出版ステータスPublished - 1997 12月

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 再生可能エネルギー、持続可能性、環境
  • 表面、皮膜および薄膜


「Effects of annealing on CuInSe2 films grown by molecular beam epitaxy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。