Fabrication and Reinforcement of Macro- and Mesoporous Bimodal Materials from Mesoporous Silica-Alumina Spheres and Their Applications to Acid Catalysts and Adsorbents

Masaki Okamoto, Yuki Takahashi, Yusuke Takanaka

研究成果: Article査読

抄録

Mesoporous silica-alumina spheres were used to create macro- and mesoporous bimodal silica-aluminas. Before removing the surfactant template for mesopores, the silica-alumina spheres were neatly stacked by sedimentation, and the contact points between the spheres were reinforced by silica. The bimodal silica-alumina was used as an acid catalyst for transesterification of triglyceride with methanol. The bimodal catalyst was readily separated from the reaction mixture. It showed the same catalytic activity as the non-sedimented spheres and higher activity than the catalyst prepared by pelletizing the silica-alumina spheres with colloidal silica binders. The bimodal materials were utilized as an adsorbent with an indicator of adsorption amount since the color changed with the amount of toluene that was adsorbed on them.

本文言語English
ページ(範囲)39-47
ページ数9
ジャーナルCatalysis Surveys from Asia
27
1
DOI
出版ステータスPublished - 2023 3月

ASJC Scopus subject areas

  • 触媒
  • 化学 (全般)

フィンガープリント

「Fabrication and Reinforcement of Macro- and Mesoporous Bimodal Materials from Mesoporous Silica-Alumina Spheres and Their Applications to Acid Catalysts and Adsorbents」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル