T1 - Hydrothermal Synthesis of Needle-like Apatite Crystal
AU - Yoshimura, Masahiro
AU - Suda, Hiroyuki
AU - Okamoto, Kengo
AU - Ioku, Koji
PY - 1991
Y1 - 1991
N2 - Hydrothermal syntheses enable us to prepare HAp crystals with various aspect ratios. HAp crystals 50 nm x145 nm, aspect ratio = 2.9) were crystallized from the HAp precursor precipitated from Ca(OH)2 and H3PO4 solutions at 200 °C under 2MPa for 5 h. Among the experimental factors, adding additives are most effective to control the aspect ratio. KOH, K3PO4 and EDTA gave needle-like HAp; aspect ratio = 63 7 and 11, respectively under the similar hydrothermal conditions.
AB - Hydrothermal syntheses enable us to prepare HAp crystals with various aspect ratios. HAp crystals 50 nm x145 nm, aspect ratio = 2.9) were crystallized from the HAp precursor precipitated from Ca(OH)2 and H3PO4 solutions at 200 °C under 2MPa for 5 h. Among the experimental factors, adding additives are most effective to control the aspect ratio. KOH, K3PO4 and EDTA gave needle-like HAp; aspect ratio = 63 7 and 11, respectively under the similar hydrothermal conditions.
UR - http://www.scopus.com/inward/record.url?scp=85016537042&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85016537042&partnerID=8YFLogxK
U2 - 10.1246/nikkashi.1991.1402
DO - 10.1246/nikkashi.1991.1402
M3 - Article
AN - SCOPUS:85016537042
SN - 0369-4577
VL - 1991
SP - 1402
EP - 1407
JO - Nippon Kagaku Kaishi
JF - Nippon Kagaku Kaishi
IS - 10
ER -