Pyrolytic synthesis and Eu³⁺→Eu²⁺ reduction process of blue-emitting perovskite-type BaLiF₃:Eu thin films

Perovskite-type barium lithium fluoride (BaLiF₃) was synthesized by pyrolysis of metal trifluoroacetates. The reaction temperature necessary for producing a single-phase material was found to be 600°C, which was lower than that for a conventional solid-state reaction or a melting method. Eu-doped BaLiF₃ was also prepared and characterized to examine the suitability of trifluoroacetates for precursors in synthesizing homogeneous complex metal fluoride materials. It was demonstrated that trivalent Eu³⁺, which was used as acetate for a starting material, was reduced to divalent Eu²⁺ in the pyrolysis process of BaLiF ₃, as indicated by a broad blue emission due to an allowed 4f ⁶5d→4f⁷ transition at 408nm with a ultraviolet excitation at 254nm. The concentration quenching of the blue emission occurred at 5at% of Eu in BaLiF₃, indicating that Eu was homogeneously dispersed in the BaLiF₃ host lattice. Mechanisms of the formation and reduction process of BaLiF₃ were discussed based on pertinent chemical reactions.