Structure and optical properties of (Gd,Eu)F3-nanocrystallized sol-gel silica films

Shinobu Fujihara, Shinnosuke Koji, Toshio Kimura

研究成果: Article査読

51 被引用数 (Scopus)


Transparent, luminescent sol-gel silica films were fabricated on the basis of a SiO2-(Gd,Eu)F3 nanocomposite structure, in which (Gd,Eu)F3 nanocrystals were dispersed in a silica matrix. The films were coated on silica glass substrates at low temperatures of 300-500°C using trifluoroacetic acid as a fluorine source. Doping Eu3+ ions into the films led to narrow emission lines upon ultraviolet (UV) excitation, indicating that Eu3+ was selectively incorporated into the GdF 3 or GdOF nanocrystals. While magnetic dipole 5D 07F1 transitions were dominant in the SiO2-(Gd,Eu)F3 films that were heat-treated at 300 or 400°C, forced electric dipole 5D07F2 transitions had a higher probability in the SiO 2-(Gd,Eu)OF film that was heat-treated at 500°C. The efficiency of the UV light excitation at 274 and 256 nm was promoted by the energy transfer from Gd3+ to Eu3+ and the charge transfer from O 2- to Eu3+ in photoluminescence, respectively.

ジャーナルJournal of Materials Chemistry
出版ステータスPublished - 2004 4月 21

ASJC Scopus subject areas

  • 化学一般
  • 材料化学


「Structure and optical properties of (Gd,Eu)F3-nanocrystallized sol-gel silica films」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。